PVA Series
Production Capability
PVA6.5PVA40300300080100(mol/mol)3.090mPa.s
Our production capacity is at 65,000 tons per year, with more than 40 varieties. We have been able to provide various specifications of granulated or crushed series of PVA products in the range of the polymerization degree at 300-3000 and the alcoholysis degree at 80-100(mol/mol)%, viscosity at 3.0-90mPa.s,and are able capable of developing and manufacturing multiple usage of and special-purpose types of PVA products with different polymerization degrees and alcoholysis degrees as requested by customers.
PVA Complete alcoholysis PVA
Products standard
Complete alcoholysis PVA series are to follow the enterprise standards Q/SH1115 105-2003 or the National standard GB12010.2-89
|
|
%mol/mol |
mPa.s | % | % | PH |
% | |
| PVA 0399 |
| 98.099.0 | 3.54.5 | 5 | 0.7 | 57 | 93.0 |
| 98.099.8 | 3.05.0 | 6 | 0.7 | 57 | 92.0 | ||
| 98.0100 | 3.05.0 | 8 | 1.0 |
| 90.0 | ||
PVA 0599 |
| 98.099.0 | 5.06.5 | 5 | 0.7 | 57 | 93.0 | |
| 98.099.8 | 4.57.0 | 6 | 0.7 | 57 | 92.0 | ||
| 98.0100 | 4.57.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1099 |
| 98.099.0 | 9.011.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 8.012.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 8.012.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1399 |
| 98.099.0 | 13.017.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 12.018.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 12.018.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1599 |
| 98.099.0 | 18.022.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 17.023.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 17.023.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1799A |
| 98.099.0 | 23.028.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 22.028.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.099.8 | 22.028.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1899 |
| 98.099.0 | 28.032.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 26.034.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 26.034.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2099 |
| 98.099.0 | 34.039.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 34.040.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 34.040.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2299 |
| 98.099.0 | 42.048.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 40.050.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 40.050.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2499 |
| 98.099.0 | 55.065.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 54.065.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 54.065.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2699 |
| 98.099.0 | 67.075.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 66.075.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 66.075.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2899 |
| 98.099.0 | 77.085.0 | 5 | 0.5 | 57 | 93.5 | |
| 98.099.8 | 76.085.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 76.085.0 | 8 | 1.0 |
| 90.0 | ||
PVA 17-99S |
| 99.8-100 | 22.0-28.0 | 8.0 | 0.7 | - | - | |
| 99.8-100 | 22.0-30.0 | 9.0 | 1.0 | - | - | ||
| 99.8-100 | 21.0-31.0 | 10.0 | 1.5 | - | - | ||
% | ||||||||
type | Item | Alcoholysis %mol/mol | Viscosity mPa.s | Volatiles % | Ash % | PH | Purity % | |
complete alcoholysis
| PVA 0399 | Excellent | 98.099.0 | 3.54.5 | 5 | 0.7 | 57 | 93.0 |
First-class | 98.099.8 | 3.05.0 | 6 | 0.7 | 57 | 92.0 | ||
Quality | 98.0100 | 3.05.0 | 8 | 1.0 |
| 90.0 | ||
PVA 0599 | Excellent | 98.099.0 | 5.06.5 | 5 | 0.7 | 57 | 93.0 | |
First-class | 98.099.8 | 4.57.0 | 6 | 0.7 | 57 | 92.0 | ||
Quality | 98.0100 | 4.57.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1099 | Excellent | 98.099.0 | 9.011.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 8.012.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 8.012.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1399 | Excellent | 98.099.0 | 13.017.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 12.018.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 12.018.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1599 | Excellent | 98.099.0 | 18.022.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 17.023.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 17.023.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1799A | Excellent | 98.099.0 | 23.028.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 22.028.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.099.8 | 22.028.0 | 8 | 1.0 |
| 90.0 | ||
PVA 1899 | Excellent | 98.099.0 | 28.032.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 26.034.0 | 6 | 0.7 | 57 | 92.5 | ||
| 98.0100 | 26.034.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2099 | Excellent | 98.099.0 | 34.039.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 34.040.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 34.040.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2299 | Excellent | 98.099.0 | 42.048.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 40.050.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 40.050.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2499 | Excellent | 98.099.0 | 55.065.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 54.065.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 54.065.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2699 | Excellent | 98.099.0 | 67.075.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 66.075.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 66.075.0 | 8 | 1.0 |
| 90.0 | ||
PVA 2899 | Excellent | 98.099.0 | 77.085.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 98.099.8 | 76.085.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 98.0100 | 76.085.0 | 8 | 1.0 |
| 90.0 | ||
PVA 17-99S | Excellent | 99.8-100 | 22.0-28.0 | 8.0 | 0.7 | - | - | |
First-class | 99.8-100 | 22.0-30.0 | 9.0 | 1.0 | - | - | ||
Quality | 99.8-100 | 21.0-31.0 | 10.0 | 1.5 | - | - | ||
Remark: In this table, % indicates mole fraction for Alcoholysis and quality index. indicates | ||||||||
Appearance: white or light yellow sheet, granular or crushed.
Products properties: high viscosity and strong adhesion; easy to film forming, good water-resistance; hard to rewet and re-adhere; high degree of crystallinity and purity, it is the best adhesive making.
Usage: It is manly used for the feedstock of vinylon fibre, PVB, textile size, paper sizing glue, pigment carrier, paper glue, adhesive of Construction coating, building material glue, film, stabilizing agent for polyvinyl acetate emulsion, PVA rubber.
preference temperature
PVA Items | 17-99 18-99 20-99 24-99 26-99 28-99 | 03-99 05-99 08-99 10-99 13-99 15-99 |
temperature | 95 | 9097 |
PVA Middle alcoholysis PVA
products standard
Middle alcoholysis PVA series are to follow the enterprise standards Q/SH1115 105-2003 or the National standard GB12010.2-89
|
|
%(mol/mol)), |
mPa.s | % , |
%, | PH |
%, | |
| PVA 1098 |
| 97.099.0 | 8.012.0 | 5 | 0.5 | 57 | 93.5 |
| 97.099.0 | 8.012.0 | 6 | 0.7 | 57 | 92.5 | ||
| 97.099.0 | 8.012.0 | 8 | 0.7 |
| 90.0 | ||
PVA 1897 |
| 96.098.0 | 27.031.0 | 5 | 0.5 | 57 | 93.5 | |
| 96.098.0 | 26.032.0 | 6 | 0.7 | 57 | 92.5 | ||
| 96.098.0 | 26.032.0 | 8 | 0.7 |
| 90.0 | ||
PVA 2497 |
| 96.098.0 | 54.064.0 | 5 | 0.5 | 57 | 93.5 | |
| 96.098.0 | 53.065.0 | 6 | 0.7 | 57 | 92.5 | ||
| 96.098.0 | 53.065.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2897 |
| 96.098.0 | 74.083.0 | 5 | 0.5 | 57 | 93.5 | |
| 96.098.0 | 74.084.0 | 6 | 0.7 | 57 | 92.5 | ||
| 96.098.0 | 74.084.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 3097 |
| 96.098.0 | 85.095.0 | 5 | 0.5 | 57 | 93.5 | |
| 96.098.0 | 84.096.0 | 6 | 0.7 | 57 | 92.5 | ||
| 96.098.0 | 84.096.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1895 |
| 94.096.0 | 26.030.0 | 5 | 0.5 | 57 | 93.5 | |
| 94.096.0 | 25.031.0 | 6 | 0.7 | 57 | 92.5 | ||
| 94.096.0 | 25.031.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1493 |
| 92.594.5 | 14.518.5 | 5 | 0.5 | 57 | 93.5 | |
| 91.095.0 | 13.019.0 | 6 | 0.7 | 57 | 92.5 | ||
| 91.095.0 | 13.019.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2092 |
| 91.093.0 | 28.034.0 | 5 | 0.5 | 57 | 93.5 | |
| 90.094.0 | 27.035.0 | 6 | 0.5 | 57 | 92.5 | ||
| 90.094.0 | 27.035.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2492 |
| 91.093.0 | 45.055.0 | 5 | 0.5 | 57 | 93.5 | |
| 90.094.0 | 44.056.0 | 6 | 0.5 | 57 | 92.5 | ||
| 90.094.0 | 44.056.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1792 |
| 91.093.0 | 21.027.0 | 5.0 | 0.5 | 57 |
| |
| 90.094.0 | 20.028.0 | 8.0 | 0.7 | 57.5 |
| ||
| 90.094.0 | 20.030.0 | 10.0 | 1.0 | 57.5 |
| ||
PVA 1795 |
| 94.096.0 | 22.028.0 | 7.0 | 0.5 | 57 |
| |
| 94.096.0 | 21.029.0 | 8.0 | 0.7 | 57.5 |
| ||
| 94.096.0 | 20.030.0 | 10.0 | 1.0 | 57.5 |
| ||
PVA 1797 |
| 96.098.0 | 23.029.0 | 7.0 | 0.7 | 57 |
| |
| 96.098.0 | 22.030.0 | 8.0 | 1.0 | 57 |
| ||
| 96.098.0 | 21.031.0 | 10.0 | 1.5 | 58 |
| ||
% | ||||||||
Type | Iten | Alcoholysis %(mol/mol)) | Viscosity mPa.s Viscosity
mPa.s | Volatiles % % , | Ash %, | PH | Purity %, | |
Middle alcoholysis
| PVA 1098 | Excellent excellent | 97.099.0 | 8.012.0 | 5 | 0.5 | 57 | 93.5 |
First Class | 97.099.0 | 8.012.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 97.099.0 | 8.012.0 | 8 | 0.7 |
| 90.0 | ||
PVA 1897 | Excellent
| 96.098.0 | 27.031.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 96.098.0 | 26.032.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 96.098.0 | 26.032.0 | 8 | 0.7 |
| 90.0 | ||
PVA 2497 | Excellent
| 96.098.0 | 54.064.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 96.098.0 | 53.065.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 96.098.0 | 53.065.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2897 | Excellent
| 96.098.0 | 74.083.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 96.098.0 | 74.084.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 96.098.0 | 74.084.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 3097 | Excellent
| 96.098.0 | 85.095.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 96.098.0 | 84.096.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 96.098.0 | 84.096.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1895 | Excellent
| 94.096.0 | 26.030.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 94.096.0 | 25.031.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 94.096.0 | 25.031.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1493 | Excellent
| 92.594.5 | 14.518.5 | 5 | 0.5 | 57 | 93.5 | |
First Class | 91.095.0 | 13.019.0 | 6 | 0.7 | 57 | 92.5 | ||
Quality | 91.095.0 | 13.019.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2092 | Excellent
| 91.093.0 | 28.034.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 90.094.0 | 27.035.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 90.094.0 | 27.035.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2492 | Excellent
| 91.093.0 | 45.055.0 | 5 | 0.5 | 57 | 93.5 | |
First Class | 90.094.0 | 44.056.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 90.094.0 | 44.056.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1792 | Excellent
| 91.093.0 | 21.027.0 | 5.0 | 0.5 | 57 |
| |
First Class | 90.094.0 | 20.028.0 | 8.0 | 0.7 | 57.5 |
| ||
Quality | 90.094.0 | 20.030.0 | 10.0 | 1.0 | 57.5 |
| ||
PVA 1795 | Excellent
| 94.096.0 | 22.028.0 | 7.0 | 0.5 | 57 |
| |
First Class | 94.096.0 | 21.029.0 | 8.0 | 0.7 | 57.5 |
| ||
Quality | 94.096.0 | 20.030.0 | 10.0 | 1.0 | 57.5 |
| ||
PVA 1797 | Excellent
| 96.098.0 | 23.029.0 | 7.0 | 0.7 | 57 |
| |
First Class | 96.098.0 | 22.030.0 | 8.0 | 1.0 | 57 |
| ||
Quality | 96.098.0 | 21.031.0 | 10.0 | 1.5 | 58 |
| ||
Remark: In this table, % indicates mole fraction for Alcoholysis and quality index.
| ||||||||
Appearance: white or light yellow sheet, granular of crushed.
Products properties: it is easily to dissolve, with strong frost resistance and the ability to binding to other materials.
Usage: It is manly used for the textile sizing, paper glue, paper sizing glue, pigment adhesive, veneer adhesive, adhesive of Construction coating, stabilizing agent for polyvinyl acetate emulsion, feedstock of vinylon fibre and the agent of textile finishing.
11.5/2
Solution Method: directly insufflate 1-1.5kg/cm2 steam to heat. Avoid to heat by open fire directly, as the bottom of container will burn because of the poor mixing.
preference temperature
PVA Items | 17-97 18-97 20-97 24-92 28-97 30-97 | 10-92 17-92 17-95 18-95 20-92 |
Temperature | 9097 | 7590 |
Way of Defoaming: in case of any foam, close the steam and temporarily cease the agitation, after the foams disappear by themselves, then rise the temperature gradually and start the agitation. The foams can be reduced significantly after repeating like this for two or three times. Apply antifoamer if necessary, (e.g. n-octyl alcoho TBP, polyethers), with the dosage generally at 0.01-0.05%.
PVA Partially Alcoholysis PVA
products standard
Partially alcoholysis PVA series are to follow the enterprise standards Q/SH1115 105-2003 or the National standard GB12010.2-89
|
|
%(mol/mol,% |
mPa.s | % , | % , | PH |
%, | |
| PVA 0388 |
| 87.089.0 | 3.04.0 | 5 | 0.7 | 57 | 93.0 |
| 86.090.0 | 3.04.5 | 6 | 0.7 | 57 | 92.0 | ||
| 86.090.0 | 3.04.5 | 8 | 1.0 | 57 | 90.0 | ||
PVA 0588 |
| 87.089.0 | 4.56.0 | 5 | 0.7 | 57 | 93.0 | |
| 86.090.0 | 4.56.5 | 6 | 0.7 | 57 | 92.0 | ||
| 86.090.0 | 4.56.5 | 8 | 1.0 | 57 | 90.0 | ||
PVA 0888 |
| 87.089.0 | 6.57.5 | 5 | 0.7 | 57 | 93.0 | |
| 86.090.0 | 6.58.0 | 6 | 0.7 | 57 | 92.0 | ||
| 86.090.0 | 6.58.0 | 8 | 1.0 | 57 | 90.0 | ||
PVA 1088 |
| 87.089.0 | 8.010.0 | 5 | 0.5 | 57 | 93.5 | |
| 86.090.0 | 8.011.0 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 8.011.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1388 |
| 87.089.0 | 12.014.0 | 5 | 0.5 | 57 | 93.5 | |
| 86.090.0 | 11.514.5 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 11.514.5 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1588 |
| 87.089.0 | 15.019.0 | 5 | 0.5 | 57 | 93.5 | |
| 87.090.0 | 14.519.5 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 14.519.5 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1888 |
| 87.089.0 | 24.028.0 | 5 | 0.5 | 57 | 93.5 | |
| 86.090.0 | 23.528.5 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 23.528.5 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2088 |
| 87.089.0 | 29.034.0 | 5 | 0.5 | 57 | 93.5 | |
| 86.090.0 | 28.035.0 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 28.035.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2288 |
| 87.089.0 | 38.042.0 | 5 | 0.5 | 57 | 93.5 | |
| 86.090.0 | 36.042.0 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 36.042.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2488 |
| 87.089.0 | 45.055.0 | 5 | 0.5 | 57 | 93.5 | |
| 86.090.0 | 44.055.0 | 6 | 0.5 | 57 | 92.5 | ||
| 86.090.0 | 44.055.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2484 |
| 83.085.0 | 42.054.0 | 5 | 0.5 | 57 | 93.5 | |
| 82.086.0 | 41.055.0 | 6 | 0.5 | 57 | 92.5 | ||
| 82.086.0 | 41.055.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1780 |
| 79.081.0 | 19.025.0 | 5 | 0.5 | 57 | 93.5 | |
| 78.082.0 | 18.026.0 | 6 | 0.5 | 47 | 92.5 | ||
| 78.082.0 | 18.026.0 | 8 | 0.7 | 47 | 90.0 | ||
PVA 2480 |
| 79.081.0 | 40.048.0 | 5 | 0.5 | 57 | 93.5 | |
| 78.082.0 | 38.050.0 | 6 | 0.5 | 47 | 92.5 | ||
| 78.082.0 | 38.050.0 | 8 | 0.7 | 47 | 90.0 | ||
PVA 1788 |
| 87.089.0 | 20.524.5 | 5.0 | 0.4 | 57 | - | |
| 86.090.0 | 20.026.0 | 8.0 | 0.7 | 57 | - | ||
| 86.090.0 | 20.026.0 | 10.0 | 1.0 | 57 | - | ||
% | ||||||||
type | Item | Alcoholysis %mol/mol | Viscosity mPa.s | Volatiles % | Ash % | PH | Purity % | |
Partially alcoholysis
| PVA 0388 | Excellent | 87.089.0 | 3.04.0 | 5 | 0.7 | 57 | 93.0 |
First-class | 86.090.0 | 3.04.5 | 6 | 0.7 | 57 | 92.0 | ||
Quality | 86.090.0 | 3.04.5 | 8 | 1.0 | 57 | 90.0 | ||
PVA 0588 | Excellent | 87.089.0 | 4.56.0 | 5 | 0.7 | 57 | 93.0 | |
First-class | 86.090.0 | 4.56.5 | 6 | 0.7 | 57 | 92.0 | ||
Quality | 86.090.0 | 4.56.5 | 8 | 1.0 | 57 | 90.0 | ||
PVA 0888 | Excellent | 87.089.0 | 6.57.5 | 5 | 0.7 | 57 | 93.0 | |
First-class | 86.090.0 | 6.58.0 | 6 | 0.7 | 57 | 92.0 | ||
Quality | 86.090.0 | 6.58.0 | 8 | 1.0 | 57 | 90.0 | ||
PVA 1088 | Excellent | 87.089.0 | 8.010.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 86.090.0 | 8.011.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 8.011.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1388 | Excellent | 87.089.0 | 12.014.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 86.090.0 | 11.514.5 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 11.514.5 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1588 | Excellent | 87.089.0 | 15.019.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 87.090.0 | 14.519.5 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 14.519.5 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1888 | Excellent | 87.089.0 | 24.028.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 86.090.0 | 23.528.5 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 23.528.5 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2088 | Excellent | 87.089.0 | 29.034.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 86.090.0 | 28.035.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 28.035.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2288 | Excellent | 87.089.0 | 38.042.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 86.090.0 | 36.042.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 36.042.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2488 | Excellent | 87.089.0 | 45.055.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 86.090.0 | 44.055.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 86.090.0 | 44.055.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 2484 | Excellent | 83.085.0 | 42.054.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 82.086.0 | 41.055.0 | 6 | 0.5 | 57 | 92.5 | ||
Quality | 82.086.0 | 41.055.0 | 8 | 0.7 | 57 | 90.0 | ||
PVA 1780 | Excellent | 79.081.0 | 19.025.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 78.082.0 | 18.026.0 | 6 | 0.5 | 47 | 92.5 | ||
Quality | 78.082.0 | 18.026.0 | 8 | 0.7 | 47 | 90.0 | ||
PVA 2480 | Excellent | 79.081.0 | 40.048.0 | 5 | 0.5 | 57 | 93.5 | |
First-class | 78.082.0 | 38.050.0 | 6 | 0.5 | 47 | 92.5 | ||
Quality | 78.082.0 | 38.050.0 | 8 | 0.7 | 47 | 90.0 | ||
PVA 1788 | Excellent | 87.089.0 | 20.524.5 | 5.0 | 0.4 | 57 | - | |
First-class | 86.090.0 | 20.026.0 | 8.0 | 0.7 | 57 | - | ||
Quality | 86.090.0 | 20.026.0 | 10.0 | 1.0 | 57 | - | ||
Remark: In this table, % indicates mole fraction for Alcoholysis and quality index.
| ||||||||
Appearance: white or light yellow sheet, granular of crushed solid.
Products properties: it is easily to dissolve, with strong frost resistance, good liquidity and stable viscosity, good hygroscopic and strong re-adhesion, and it contains many hydrophobic groups to bind with other hydrophobic materials.
:
Usage: It is manly used for the textile sizing, paper glue, paper sizing glue, pigment carrier, adhesive of Construction coating, additive and adhesive of construction material, coating agent of seed and medicine, adhesive of inorganic and electronic products, water-soluble film, makeup additive, stabilizing agent for polyvinyl acetate emulsion and suspension polymerization of vinyl chloride.
Heating method: directly insufflate 1-1.5kg/cm2 steam to heat. Avoid to heat by open fire directly, as the bottom of container will burn because of the poor mixing.
preference temperature
PVA items | 24-88 22-88 17-88 10-88 08-88 | 24-80 17-80 03-88 05-88 |
temperature | 6585 | 55 |
Way of Defoaming: in case of any foam, close the steam and temporarily cease the agitation, after the foams disappear by themselves then rise the temperature gradually and start the agitation. The foams can be reduced significantly after repeating like this for two or three times. Apply antifoamer if necessary, (e.g. n-octyl alcoho TBP, polyethers), with the dosage generally at 0.01-0.05%.
PVBSFPVB (SF series)
PVB series are to follow the enterprise standards Q/SH1115 105-2003
|
| |
|
| |
|
| |
mol/mol | 99.3-99.6 | 99.0-99.3 |
mPa.s | 28.5-30.5 | 28.0-30.0 |
% | 5 | 5 |
% | 0.3 | 0.4 |
PH | 5-7 | 5-7 |
|
| 175050 |
| ||
ITEMS | Index | |
Type I | Type | |
Excellent | Excellent | |
Alcoholysis mol/mol | 99.3-99.6 | 99.0-99.3 |
Viscosity mPa.s | 28.5-30.5 | 28.0-30.0 |
Volatile % | 5 | 5 |
Ash % | 0.3 | 0.4 |
PH | 5-7 | 5-7 |
The degree of average polymerization |
| 175050 |
Remark: In this table, % indicates mole fraction for Alcoholysis and quality index. | ||
Appearance: white granalur.
Products properties:
1. Narrow range of alcoholysis to control acetalation.
2. Narrow range of polymerization to stable the products viscosity.
3. Poor contents of ash and impurity to improve the purity of products.
PVBPVAPVB
Usage: It is mainly used as the film in laminated glass, used in automobiles, planes and high-rise window glass.
Remarks: we can produce the PVB special materials as customers required.
PVA PVA special materials for textile sizing
Products standard
PVA special materials for textile sizing series are to follow the enterprise standards Q/SH1115 105-2003
|
| |
|
| |
|
| |
mol/mol | 92.1-95.4 | 92.1-95.4 |
mPa.s | 10-15 | 12-17 |
% | 5 | 5 |
PH | 5-7 | 5-7 |
| 1.0 | 1.0 |
1 24%2520 | ||
Items | Index | |
Type I | Type | |
excellent | excellent | |
Alcoholysis mol/mol | 92.1-95.4 | 92.1-95.4 |
Viscosity mPa.s | 10-15 | 12-17 |
Volatile % | 5 | 5 |
PH | 5-7 | 5-7 |
Sodium acetate | 1.0 | 1.0 |
Remark: 1.In this table, % indicates mole fraction for Alcoholysis and quality index. 2.test conditionSolution concentration 4%testing temperature: Type I 25Type20
| ||
Appearance: Type I is white powder, Type II is white granular.
properties comparative testing
The mixed viscosity of PVA1799 and PVA0588 compares with the viscosity of textile sizing
| PVA0588 % | PVA1799 % |
mPa.s | PVA mPa.s |
1 | 5 | 95 | 24.85 |
10-15 12-17 |
2 | 10 | 90 | 22.35 | |
3 | 15 | 85 | 21.05 | |
4 | 20 | 80 | 19.35 | |
5 | 30 | 70 | 16.50 | |
6 | 40 | 60 | 13.65 | |
7 | 50 | 50 | 10.90 | |
14%25 | ||||
NO. | PVA0588 % | PVA1799 % | The mixed viscosity mPa.s | Textile sizing viscosity mPa.s |
1 | 5 | 95 | 24.85 |
Type 10-15 Type 12-17 |
2 | 10 | 90 | 22.35 | |
3 | 15 | 85 | 21.05 | |
4 | 20 | 80 | 19.35 | |
5 | 30 | 70 | 16.50 | |
6 | 40 | 60 | 13.65 | |
7 | 50 | 50 | 10.90 | |
Testing condition of Type ISolution concentration 4%testing temperature 25 | ||||
Products properties:
It is easily to dissolve, and with high concentration and low viscosity. Its viscosity is equivalent to the mixed viscosity of 30%PVA0588 and 70% PVA1799. Its skin membrane is soft, which can be helpful for secondary leasing, and hard to damage the yarn and regenerate hairiness. With good permeability and easy sizing, it can improve the wearability of yarn. It is not easy to crust in winter because of the less crustification. The properties of low hygroscopic and re-viscosity can improve the antistatic when weave in the humidity environment, and uneasy to pilling in weaving thus increasing the efficiency. It is easy to desizing.
Usage: it is apply to high concentration and low viscosity under high-pressure sizing process, also to thin and close fabric sizing and polyester-cotton (more polyester contents) sizing.
Remarks: we can produce the PVB special materials as customers required.
PVA packing, storage, transportation
There are two main ways of packing: small bags and big bags. The small is packed in plastic woven bag (with inner liners of plastic film) or paper-plastic bag,the inner is roped with rope, and the outer is sewed with strings , 25kg net weight each bag if plastic woven package; or is seamed and hot sealed by automatic packaging machine, 20kg or 15kg net weight each bag if paper-plastic package. The big is packed in woven bags and taped with plastic rope, 500-1000kgs net weight. And the package can be done according the requests of clients.
The packing shall be printed on clear and firm trademarks, indicating products name, type, grade, lot number, net weight, date of production and the manufacturer name and address, each lot of the products should be attached with the Certificate of Quality (COQ), indicating grade, batch No. and inspection No..
The storage place should be dry, good ventilating, with indoor temperature 5-30. The products should not be putted near the radiator or any other heat sources and should be strictly prohibited to put together with volatile chemical materials to prevent from deterioration. The products should also be prevented from sunshine and wet.
PVA products should be transported in clean vehicles with shelters to prevent from damp, rain and sunshine. Handle with cares in case of and scratches of damages.
Regulations of acceptance
Each batch of PVA will be inspected by our inspection department to ensure the products with corresponding quality standard or contract standard.
Each lot of the products should be attached with the Certificate of Quality (COQ), which contains: products name, batch No, date of production, standard No. and the manufacturers name and address.
The users have the right to test and /or check PVA products according to the standard stipulations of the products or contract standard before acceptance. If there are objection for the products quality, the users should notify us within one month after received the goods. The case will be negotiated by two parties or arbitrated by arbitration institute. If the products have been used more than one third, it will not be applied for retesting.
The inspection method of acceptance should be corresponding to the products standard.
Remarks
Since it is regulated by the state that product quality standards of enterprise shall be revised every three year, or some indexes may be changed in accordance with market requirements, therefore customers should seek for up-to dated quality standards from the sales department at any time.